EVA self-adhesive waterproof roll adopts synthetic high polymer EVA processing composite sheet, high polymer and modified high-quality asphalt as the base material. The composite new synthetic high polymer waterproof roll with excellent waterproof performance has the waterproof performance of high polymer waterproof roll and self-adhesive waterproof roll. One layer of roll, two layers of fortification, greatly improves the waterproof effect of the waterproof layer. EVA self-adhesive waterproof roll can be divided into non tire base (n type) and polyester tire base (py type).
1. Product features
① It can be constructed in low temperature and humid environment;
② It has good adhesive sealing, puncture resistance and self-healing, high elongation, non-toxic and tasteless products, which meet the requirements of environmental protection.
2. Product specifications
(1) Mass and thickness per unit area of class n
EVA self-adhesive waterproof roll type N specification and dimension of mass and thickness per unit area (GB 23441-2009) table 3-23
Thickness specification 1.2 1.5 2.0
Upper surface materials PE, pet, DPE, pet, DPEX pet, D
1.21.52.0 more children per unit area (kym3)
Thickness (RRNN) average > 1.21.52.0
Minimum single value 1.0 1.3 1.7
(2) Quality and thickness per unit area of Py (table 3-24)
EVA self-adhesive waterproof roll py type specification and size of quality and thickness per unit area (GB 2344-2009) table 3-24
Thickness specification 2.0 3.0 4.0
Upper surface material PE, DS PE, DS PE, DS
Mass disc per unit area (kg / m3) ^ 2.12.2 3.13.2 4.14.2
The average thickness (mm) is 2.03.04.0
Minimum single value 1.8 2.7 3.7
3. Quality index
(1) EVA self-adhesive waterproof roll, class n (table 3-25)
Table 3-25 physical properties of EVA self-adhesive waterproof roll type n (GB 23441-2009)
Index B of item No
PE PET D
I n 1 H
1 tensile strength tensile force (n / 50mm) > 150 200 150 200 one
Extension dimension (%) ^ 200 30 when carrying large tension
Asphalt elongation at break (%) 5 = 250 150 450
Phenomenon during stretching, especially the separation of asphalt coating and membrane before membrane rupture
2. Nail bar tear strength (n) ^ 60 110 30 40 -
3 heat resistance 70t, sliding not more than 2mm
4. Low temperature flexibility (1) - 20-30-20-30-20, no crack
5 impermeability: 0.2MPa, 120min